Galvanized Steel Coil
Hot-dip galvanizing is the reaction of molten metal with an iron substrate to produce an alloy layer, thereby combining the substrate and the plating layer. Hot-dip galvanizing is to pickle iron and steel parts first. In order to remove iron oxide on the surface of iron and steel parts, after pickling, it is cleaned in an ammonium chloride or zinc chloride aqueous solution or a mixed solution of ammonium chloride and zinc chloride.And then sent to the hot-dip plating bath. Hot-dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.
| Standard | AISI,ASTM,GB,JIS | Material | SGCC,S350GD+Z,S550GD+Z,DX51D,DX52D,DX53D |
| Thickness | 0.16-5mm | Width | 600-1250mm |
| Tolerance | +/-0.02mm | Zinc coating | 60-275g/m2 |
| Coil ID | 508-610MM | Coil Weight | 3-8 tons |
| Technique | Hot rolled, cold rolled | Package | seaworthy package |
| Certification | ISO 9001-2008,SGS,CE,BV | MOQ | 25 TONS (in one 20ft FCL) |
| Delivery | 15-20 days | Monthly Output | 10000 tons |
| Surface treatment: | oiled, passivation or chromium-free passivation, passivation+oiled, chromium-free passivation+oiled, resistant to fingerprints or chromium-free resistant to fingerprints | ||
| Spangle | regular spangle,minimal spangle, zero spangle,big spangle | ||
| Payment | 30%T/T in advanced+70% balanced;irrevocable L/C at sight | ||
| Remarks | Insurance is all risks and accept the third party test | ||
| Mechanical properties of galvanized steel | |||
| Usage | Grade | Yield strength(MPa) | Tensile strength(MPa) |
| Punching galvnaized steel | DC51D+Z | - | 270-500 |
| DC52D+Z | 140-300 | 270-420 | |
| DC53D+Z | 140-260 | 270-380 | |
| Structure galvanized steel | S280GD+Z | ≥280 | ≥360 |
| S350GD+Z | ≥350 | ≥420 | |
| S550GD+Z | ≥550 |
≥560 |
|